FTIR and Rheology study of Alginate samples: Effect of Radiation
Mollah, Mohammad Z. I. Faruque, Mohammad R. I. Bradley, David Khandaker, Mayeen U. Al-Assaf, Saphwan
Mollah, Mohammad Z. I.
Faruque, Mohammad R. I.
Bradley, David
Khandaker, Mayeen U.
Al-Assaf, Saphwan
Advisors
Editors
Other Contributors
EPub Date
Publication Date
2022-09-04
Submitted Date
Collections
Files
Loading...
Article - AAM
Adobe PDF, 503.45 KB
Other Titles
Abstract
Two well characterised alginate samples with high and low M/G ratio were subjected to radiation decontamination dose at 15 kGy. Subsequently, a number of techniques were used to determine the effect of radiation on the gelling properties. These techniques include: (GPC-MALLS) gel permeation chromatography linked to a multi-angle laser light scattering and refractive index detector for the determination of molecular weight and distribution. To observe the mechanics, the deformation with flow of α-β alginates rheological measurements in the dynamic oscillation modes, and distinguish the functional group of the samples along with identifying the M/G ratio for quantitative determination of mannuronic and guluronic acid, the FTIR techniques were performed respectively. The results showed clear reduction in the molecular weight following irradiation which was also accompanied by a loss of the gelling properties as well as clear reduction intensity of FTIR peak at 1080-1400 cm -1 for carboxylic group, OH-bonding obtained at 1030 cm-1 (1026 and 1028 cm-1) while the weak signal and skeletal region is attributed at >2800 and < 700 cm-1 respectively. A sample (n = 1; H120L) is homopolyguluronic enriched (820 cm-1 in fingerprint region) with small amount of mannuronic acid fraction. Sample (n = 2; LFR-5/60) is heteropolyguluronic acid enriched in presence of tiny amount guluronic acid (814 cm-1 peak) i.e. comparatively high G to M in this fraction but %G is lower than n = 1. The rheological parameter storage modulus (G′ ) and loss modulus (G”) were noticed higher with the constant frequency mode, a solid-like nature gels was obtained with increasing the frequency in a certain time of relaxation. The gelling
properties of the samples calculated is M/G < 1 which able to make hard and rigid gel. Thus, radiation effects for rheology and FTIR in case of functional group distribution was significant.
Citation
Mollah, M. Z. I., Faruque, M. R. I., Bradley, D. A., Khandaker, M. U., Al-Assaf, S. (2023). FTIR and rheology study of alginate samples: Effect of radiation. Radiation Physics and Chemistry, 202, article-number 110500. https://doi.org/10.1016/j.radphyschem.2022.110500
Publisher
Elsevier
Journal
Radiation Physics and Chemistry
Research Unit
DOI
10.1016/j.radphyschem.2022.110500
PubMed ID
PubMed Central ID
Type
Article
Language
Description
Series/Report no.
ISSN
0969-806X